		title ={PENGARUH VARIASI DIAMETER KAWAT MgB2 DAN PENAMBAHAN DOPING Mg 10 mol% DENGAN MENGGUNAKAN METODE POWDER IN TUBE},
		year={2019},
		url={http://156.67.221.169/3265/},
		abstract={MgB2 superconductor wire has been applied a lot, especially in the health sector for example. Magnetic Resonance Imaging (MRI), because the MgB2 superconductor multifilament wire is a material or material that has advantages so that it can conduct electricity properly, so there is no power loss during the power distribution process. In this study the authors study the process of making superconductor multifilament wire. by using a method. Powder In Tube (P.I.T). The purpose of this study is to look at compounds / phases, resistance to critical temperature values (Tc). See how the influence of 10mol% Mg addition and diameter variation in MgB2 superconducting wire. Sintering uses a furnace with a temperature of 800OC for 2 hours. The result of the test was not obtained Tc zero karan in the sintering sample which formed porosity and formed MgO as an impurity compound.}
		}