PENGARUH PENGGUNAAN LIMBAH BETON DAN PENAMBAHAN SERBUK KAYU TERHADAP KEKUATAN BETON
Total View This Week0
Total View This Week0
Institusion
Institut Teknologi Perusahaan Listrik Negara
Author
ARNANDI, MUHAMMAD FIKRI
Dian Purnama, Dicki
Dian Purnama, Dicki
Subject
Teknik Sipil
Datestamp
2022-09-20 04:05:14
Abstract :
The powder timber is a remainder of the processing timber which according to researchers before the powder timber has a content of cellulose and hemicellulose are able to add power tie between the particles. Waste concrete has properties which together with the aggregate coarse that could be obtained on laboratory tests. In this research, Made the object of test cylinder concrete normal as control strength concrete. Strong press plan used 20 MPa. Waste concrete is a substitution of fixed aggregate coarse amounted to 25% and powder wood teak Dutch used as an ingredient added which has a size of 2 mm to 5 mm with a variety of materials added at 0%, 0.5%, 1% and 2% of the weight of the total concrete. The test parameters were the compressive strength at the age of 7, 14, and 28 days and the split tensile strength of the concrete at the age of 28 days. Based on the test obtained value of strong press at the age of 28 days that amounted to 20.382 MPa 20.665 MPa, MPa 21.137 and 20.760 MPa. And obtained the value of the strong pull apart at the age of 28 days which amounted to 2,595 MPa, 2,666 MPa, 2,736 MPa and 2,624 MPa. The variation of the mixture that gets the optimum compressive strength and split tensile strength is a variation of 25% concrete waste and the addition of 1% wood powder from the total weight of the concrete with a compressive strength value of 21.137 MPa and a split tensile strength value of 2.736 MPa.
The powder timber is a remainder of the processing timber which according to researchers before the powder timber has a content of cellulose and hemicellulose are able to add power tie between the particles. Waste concrete has properties which together with the aggregate coarse that could be obtained on laboratory tests. In this research, Made the object of test cylinder concrete normal as control strength concrete. Strong press plan used 20 MPa. Waste concrete is a substitution of fixed aggregate coarse amounted to 25% and powder wood teak Dutch used as an ingredient added which has a size of 2 mm to 5 mm with a variety of materials added at 0%, 0.5%, 1% and 2% of the weight of the total concrete. The test parameters were the compressive strength at the age of 7, 14, and 28 days and the split tensile strength of the concrete at the age of 28 days. Based on the test obtained value of strong press at the age of 28 days that amounted to 20.382 MPa 20.665 MPa, MPa 21.137 and 20.760 MPa. And obtained the value of the strong pull apart at the age of 28 days which amounted to 2,595 MPa, 2,666 MPa, 2,736 MPa and 2,624 MPa. The variation of the mixture that gets the optimum compressive strength and split tensile strength is a variation of 25% concrete waste and the addition of 1% wood powder from the total weight of the concrete with a compressive strength value of 21.137 MPa and a split tensile strength value of 2.736 MPa.
Download
book
BibTex
Latex, Jabref
cloud_download
Original Resource
url resource Institution