PENGARUH VARIASI WAKTU PERENDAMAN ALKALI KOMPOSIT
SERAT RAMI BERMATRIK POLYESTER TERHADAP KEKUATAN
BENDING DAN IMPACT
Total View This Week0
Total View This Week0
Institusion
INSTITUT TEKNOLOGI DIRGANTARA ADISUTJIPTO
Author
ALIF FIRMAN SHAH, RIYAN
Subject
T Technology (General)
Datestamp
2024-06-27 07:41:09
Abstract :
Natural Composite (NACO) is a material that could be developed in Indonesia. Mechanically bonded composites reinforced by natural fibers can be improved by chemical treatments such as the alkaline treatment. It is often used as it is more economical. The purpose of this study was to study the effect of alkaline immersion on the bending properties and impact of hemp fiber reinforced composites. The main ingredient of the research is hemp fiber and transparent polyester resin 108. The hardener used is a MEKPO hardener with a concentration of 1%. The composite is handmade. The composite consists of random hemp fibers, the volume fraction of composite fibers is 15%, the alkaline quenching solution (NaOH) 5% with time variations of 0, 1, 2, 3, 4 hours. The flexural test specimen refers to ASTM D 790-03 and the impact test to ASTM D 256-03. The fracture section is examined to identify the fracture mechanism. The results showed that the greatest flexural strength was obtained with immersion of 3 hours equal to 64,094 MPa. The highest impact resistance was obtained in fibers without alkaline immersion of 0.013 J / mm². The stages of the composite failure were tensile failure on the lower side, compression failure on the upper side, and the fiber failure on the pull out.
Natural Composite (NACO) is a material that could be developed in Indonesia. Mechanically bonded composites reinforced by natural fibers can be improved by chemical treatments such as the alkaline treatment. It is often used as it is more economical. The purpose of this study was to study the effect of alkaline immersion on the bending properties and impact of hemp fiber reinforced composites. The main ingredient of the research is hemp fiber and transparent polyester resin 108. The hardener used is a MEKPO hardener with a concentration of 1%. The composite is handmade. The composite consists of random hemp fibers, the volume fraction of composite fibers is 15%, the alkaline quenching solution (NaOH) 5% with time variations of 0, 1, 2, 3, 4 hours. The flexural test specimen refers to ASTM D 790-03 and the impact test to ASTM D 256-03. The fracture section is examined to identify the fracture mechanism. The results showed that the greatest flexural strength was obtained with immersion of 3 hours equal to 64,094 MPa. The highest impact resistance was obtained in fibers without alkaline immersion of 0.013 J / mm². The stages of the composite failure were tensile failure on the lower side, compression failure on the upper side, and the fiber failure on the pull out.
Download
book
BibTex
Latex, Jabref
cloud_download
Original Resource
url resource Institution