ANALISIS HASIL PENYAMBUNGAN STAINLESS STEEL 304 DENGAN 316L TERHADAP FACE BEND DAN ROOT BEND MENGGUNAKAN METODE PENGELASAN GTAW
Total View This Week0
Total View This Week0
Institusion
Universitas Islam 45
Author
AS'ADURROFIQ, AS'ADURROFIQ
Subject
Manufaktur
Datestamp
2022-08-01 07:50:23
Abstract :
The connection of 304 stainless steel with 316L stainless steel is carried out using GTAW welding, ER316L filler metal, joint design, current magnitude, position and other welding parameters are designed and selected and then standardized on WPS (Welding Procedure Specification), welder reports during the welding process and laboratory the test results were analyzed and recorded in the Procedure Qualification Record (PQR), the results of the Face bending test and the Root bend Face test showed that the welding results did not produce defects and or cracks along the weld area (No Open Discontinuity was Observed). ), this indicates that the weld results are acceptable in accordance with the requirements in ASME Section IX and the parameters in the WPS are considered valid for the welding case above. KeyWords: Stainless Steel 304 and 316 L, GTAW, PQR, Face and Root bent test.
The connection of 304 stainless steel with 316L stainless steel is carried out using GTAW welding, ER316L filler metal, joint design, current magnitude, position and other welding parameters are designed and selected and then standardized on WPS (Welding Procedure Specification), welder reports during the welding process and laboratory the test results were analyzed and recorded in the Procedure Qualification Record (PQR), the results of the Face bending test and the Root bend Face test showed that the welding results did not produce defects and or cracks along the weld area (No Open Discontinuity was Observed). ), this indicates that the weld results are acceptable in accordance with the requirements in ASME Section IX and the parameters in the WPS are considered valid for the welding case above. KeyWords: Stainless Steel 304 and 316 L, GTAW, PQR, Face and Root bent test.
Download
book
BibTex
Latex, Jabref
cloud_download
Original Resource
url resource Institution