Variasi Waktu Dan Tegangan Proses Elektroplating Nikel – Cromium Pada Baja Karbon Rendah Terhadap Laju Korosi Bahan Pelapis
Total View This Week0
Total View This Week0
Institusion
Politeknik Negeri Jember
Author
Pradikta, Galih Estu
Subject
431 - Teknik Mesin (dan Ilmu Permesinan Lain)
Datestamp
2021-11-11 03:36:58
Abstract :
A steel that is often seen and used in the industrial world primarily in the automotive aspect, a low carbon steel has relatively high levels of strength and very easily molded. But with relatively high power it does not required the possibility of avoiding corrosion. The Corrosion, it can only be prevented by one process of electroplating. Electroplating is a type of coating using direct electric currents and certain electrolyte compounds. The nickel coated elements for the first upholstery, then re-coated with chromium. The research was done in Bengkel Rezeki Motor. The variation?s treatment process time is 5, 10, 15 minute with the tension 30V, 40V, 50V with soaking using corrosive media of HCl 20% in 20 days. The impact of variations in time and voltage released by electroplating to the rate of corrosion the highest average thickness of 33,90 µm is found in time variation 15 minutes with 50V variations. For specimens at most cortical rate both with 15 minutes of time variations with 50V tension variations 7,64% percentage has a heavy loss on the rate of corrosion. The conclusion from a research is increasingly thickening the results of dilation using variations in time and the highest voltage, and the power to corrode is growing smaller. Keyword: Carbon steel, Corrosion, Electroplating
A steel that is often seen and used in the industrial world primarily in the automotive aspect, a low carbon steel has relatively high levels of strength and very easily molded. But with relatively high power it does not required the possibility of avoiding corrosion. The Corrosion, it can only be prevented by one process of electroplating. Electroplating is a type of coating using direct electric currents and certain electrolyte compounds. The nickel coated elements for the first upholstery, then re-coated with chromium. The research was done in Bengkel Rezeki Motor. The variation?s treatment process time is 5, 10, 15 minute with the tension 30V, 40V, 50V with soaking using corrosive media of HCl 20% in 20 days. The impact of variations in time and voltage released by electroplating to the rate of corrosion the highest average thickness of 33,90 µm is found in time variation 15 minutes with 50V variations. For specimens at most cortical rate both with 15 minutes of time variations with 50V tension variations 7,64% percentage has a heavy loss on the rate of corrosion. The conclusion from a research is increasingly thickening the results of dilation using variations in time and the highest voltage, and the power to corrode is growing smaller. Keyword: Carbon steel, Corrosion, Electroplating
Download
book
BibTex
Latex, Jabref
cloud_download
Original Resource
url resource Institution